Polycasa SPC Diamond Polycarbonate

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	Polycasa
Trade Name	SPC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polycasa SPC Diamond Polycarbonate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

QUINN SPC diamond sheets are exceptionally stiff. Sheet with a 32 mm thickness resists a load of 100 kg per m2 under normal circumstances. QUINN SPC diamond sheets have excellent light transmission values - up to 60% for 16 mm. Even in the winter, the sunlight will easily warm up the conservatory. QUINN SPC diamond sheets are treated to resist UV radiation. The conservatory roof won’t turn yellow after the first summer. On the contrary, we offer a 10 year warranty against yellowing. QUINN SPC diamond sheets are designed to have improved thermal insulation values, up to a U-value of 1.4 for 32 mm thickness. The conservatory will remain warm without excessive heat loss and heating costs will be reduced.ConservatoriesWinter gardensPergolasRoofingCladdingQuinn Manufacturing Group rebranded its Plastics Division as Polycasa in 2013.

Optical Properties	Metric	English	Comments
Transmission, Visible	16 %	16 %	Bronze, 32mm
	25 %	25 %	Bronze, 16mm
	40 %	40 %	Opal 3B, 16mm
	44 %	44 %	Opal 3B, 32mm
	34 % @Thickness 32.0 mm	34 % @Thickness 1.26 in	Cool White
	37 % @Thickness 16.0 mm	37 % @Thickness 0.630 in	Cool White
	42 % @Thickness 32.0 mm	42 % @Thickness 1.26 in	Super Cool White
	45 % @Thickness 16.0 mm	45 % @Thickness 0.630 in	Super Cool White
	57 % @Thickness 32.0 mm	57 % @Thickness 1.26 in	Clear
	60 % @Thickness 16.0 mm	60 % @Thickness 0.630 in	Clear
UV Transmittance	29 % @Thickness 32.0 mm	29 % @Thickness 1.26 in	Cool White
	34 % @Thickness 16.0 mm	34 % @Thickness 0.630 in	Cool White
	35 % @Thickness 32.0 mm	35 % @Thickness 1.26 in	Super Cool White
	40 % @Thickness 16.0 mm	40 % @Thickness 0.630 in	Super Cool White