SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* RF-1006 EP HS is based on Nylon 6/6 containing Glass Fiber. Characteristics of this grade include Exceptional Processing and Heat Stabilizer.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ASTM D 792
Density 1.43 g/cc
0.0517 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 1.3 %
1.3 %
23°C / 50% RH; ISO 62
0.84 %

@Time 86400 sec
 0.84 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 - 0.0040 cm/cm

@Time 86400 sec
 0.0010 - 0.0040 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 159 MPa
23100 psi
5 mm/min; ISO 527
163 MPa
23600 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 159 MPa
23100 psi
5 mm/min; ISO 527
163 MPa
23600 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 2.8 %
2.8 %
Type I, 5 mm/min; ASTM D 638
3.0 %
3.0 %
5 mm/min; ISO 527
Elongation at Yield 2.7 %
2.7 %
Type I, 5 mm/min; ASTM D 638
2.9 %
2.9 %
5 mm/min; ISO 527
Tensile Modulus 10.52 GPa
1526 ksi
1 mm/min; ISO 527
11.12 GPa
1613 ksi
50 mm/min; ASTM D 638
Flexural Strength 234 MPa
33900 psi
1.3 mm/min, 50 mm span; ASTM D 790
239 MPa
34700 psi
ISO 178
Flexural Yield Strength 234 MPa
33900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 8.66 GPa
1260 ksi
1.3 mm/min, 50 mm span; ASTM D 790
8.78 GPa
1270 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.940 J/cm

@Temperature 23.0 °C
 1.76 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 9.85 J/cm

@Temperature 23.0 °C
 18.5 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 60.0 kJ/m²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 34.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 18.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 84.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 46.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
256 °C

@Thickness 3.20 mm
 493 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 234 °C
453 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
241 °C

@Thickness 3.20 mm
 466 °F

@Thickness 0.126 in
 unannealed; ASTM D 648