- Resinoid 2215 Phenolic Molding, Cellulose Reinforced
Resinoid 2215 Phenolic Molding, Cellulose Reinforced
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Cellulose Filled |
| Manufacturer | Resinoid |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Resinoid 2215 Phenolic Molding, Cellulose Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792A |
| Water Absorption | 0.50 % | 0.50 % | 24 hours R.T. ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D651 |
| Flexural Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Compressive Strength | 179 MPa | 26000 psi | ASTM D695 |
| Izod Impact, Notched | 0.368 J/cm | 0.689 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.30 mm |
V-0 @Thickness 0.248 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 8.70 kV/mm | 221 kV/in | Short Time; Dry; ASTM D149 |
| Arc Resistance | 100 sec | 100 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 155 - 180 °C | 311 - 356 °F |