SABIC Innovative Plastics LNP Thermocomp RF004S PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp RF004S PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* RF004S is a Nylon 6/6 containing Glass Fiber. Characteristics are Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D 792
Density 1.30 g/cc
0.0470 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 1.6 %
1.6 %
23°C / 50% RH; ISO 62
1.0 %

@Time 86400 sec
 1.0 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Time 86400 sec
 0.0050 - 0.0080 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 121 MPa
17500 psi
Type I, 5 mm/min; ASTM D 638
121 MPa
17500 psi
5 mm/min; ISO 527
Tensile Strength, Yield 121 MPa
17500 psi
Type I, 5 mm/min; ASTM D 638
121 MPa
17500 psi
5 mm/min; ISO 527
Elongation at Break 1.9 %
1.9 %
5 mm/min; ISO 527
2.1 %
2.1 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 1.9 %
1.9 %
5 mm/min; ISO 527
2.1 %
2.1 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 7.18 GPa
1040 ksi
1 mm/min; ISO 527
7.93 GPa
1150 ksi
50 mm/min; ASTM D 638
Flexural Strength 186 MPa
27000 psi
ISO 178
188 MPa
27300 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 187 MPa
27100 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 5.34 GPa
775 ksi
1.3 mm/min, 50 mm span; ASTM D 790
5.86 GPa
850 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.500 J/cm

@Temperature 23.0 °C
 0.937 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 5.16 J/cm

@Temperature 23.0 °C
 9.67 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
7.00 J

@Temperature 23.0 °C
 5.16 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 3.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
 1.67 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 8.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
 4.44 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 253 °C
487 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
255 °C

@Thickness 3.20 mm
 491 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 226 °C
439 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
236 °C

@Thickness 3.20 mm
 457 °F

@Thickness 0.126 in
 unannealed; ASTM D 648