SABIC Innovative Plastics LNP Thermocomp Cycoloy_C7210A PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp Cycoloy_C7210A PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. Very good modulus-ductility balance.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16.4 g/10 min @Load 2.16 kg, Temperature 260 °C |
16.4 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 80 % | 80 % | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Yield | 3.6 % | 3.6 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 3.51 GPa | 509 ksi | 5 mm/min; ASTM D 638 |
| Flexural Strength | 106 MPa | 15400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 3.14 GPa | 455 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.76 J/cm @Temperature 23.0 °C |
3.30 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 18.69 J/cm @Temperature 23.0 °C |
35.01 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Impact Test | 47.0 J @Temperature 23.0 °C |
34.7 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Vicat Softening Point | 101 °C | 214 °F | Rate B/50; ASTM D 1525 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.19 mm |
V-0 @Thickness 0.0469 in |
UL 94 |
| 5VB @Thickness 1.98 mm |
5VB @Thickness 0.0780 in |
UL 94 |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CM100LN Polypropylene, Impact Copolymer, Medium Impact, Nucleated, Antistat, Injection Molding
- LG Chemical LUTENE MB9205 LDPE Injection Molding Grade
- Lucite International Diakon® ST45G6 Toughened Acrylic Polymer
- SABIC Innovative Plastics NORYL WCD801A PPE-TPE
- Stir SpA AF 84 CZ (PVC)
- Eurostar Staramide PF003U PA6, 15% Glass Fiber Filled, Injection Molded
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N774 Filler
Copyright © lookpolymers.com All Rights Reserved