SABIC Innovative Plastics LNP FARADEX PS003E PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP FARADEX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP FARADEX PS003E PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Faradex* PS003E is a compound based on Nylon 6 resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Moisture Absorption | 1.30 % | 1.30 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0072 cm/cm @Time 86400 sec |
0.0072 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527 |
| 55.0 MPa | 7980 psi | ASTM D638 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | ISO 527 |
| 55.0 MPa | 7980 psi | ASTM D638 | |
| Elongation at Break | 8.6 % | 8.6 % | ISO 527 |
| 23 % | 23 % | ASTM D638 | |
| Elongation at Yield | 3.3 % | 3.3 % | ISO 527 |
| 9.6 % | 9.6 % | ASTM D638 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| 3.15 GPa | 457 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 81.0 MPa | 11700 psi | ISO 178 |
| 82.0 MPa | 11900 psi | ASTM D790 | |
| Flexural Modulus | 2.31 GPa | 335 ksi | ASTM D790 |
| 2.40 GPa | 348 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.89 J/cm | 7.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m² | 20.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 70.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 42.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 75.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 °C | 340 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 186 °C @Thickness 3.20 mm |
367 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 62.0 °C @Thickness 3.20 mm |
144 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 ohm | 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- LyondellBasell Pro-fax SB912 Polypropylene Impact Copolymer
- Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; HT (TH04) Temper; over 25 to 51 mm Thickness (UNS C17000)
- GrafTech EN Envelope Edge-Seal
- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness
- Techmer ES Luriblend® PA6/6 TS20 HS Nylon 66
- A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66
- TIMCAL TIMREX® SFG6 Primary Synthetic Graphite
- ExxonMobil Mobil Glygoyle 100
- Arlon R30711R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics Lexan® ML1661 PC Copolymer (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved