- Hexcel® HexPly® F593 Epoxy Resin, T2G145 Carbon Tape
Hexcel® HexPly® F593 Epoxy Resin, T2G145 Carbon Tape
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F593 Epoxy Resin, T2G145 Carbon Tape.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: T2GXXX-12"-F593; Fiber: Amoco T-300/12kInformation provided by HexCel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Volatiles | 1.0 - 4.0 % | 1.0 - 4.0 % | Prepreg |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 5.288 MPa @Temperature 24.0 °C |
767.0 psi @Temperature 75.2 °F |
Sandwich Flatwise Tension, Dry |
| 1517 MPa @Temperature -54.0 °C |
220000 psi @Temperature -65.2 °F |
Dry | |
| 1731 MPa @Temperature 24.0 °C |
251100 psi @Temperature 75.2 °F |
Dry | |
| 1772 MPa @Temperature 93.0 °C |
257000 psi @Temperature 199 °F |
Dry | |
| Tensile Modulus | 119.3 GPa @Temperature 24.0 °C |
17300 ksi @Temperature 75.2 °F |
Dry |
| 126.2 GPa @Temperature -54.0 °C |
18300 ksi @Temperature -65.2 °F |
Dry | |
| 129.6 GPa @Temperature 93.0 °C |
18800 ksi @Temperature 199 °F |
Dry | |
| Compressive Yield Strength | 1248 MPa @Temperature 71.0 °C |
181000 psi @Temperature 160 °F |
Wet |
| 1372 MPa @Temperature 93.0 °C |
199000 psi @Temperature 199 °F |
Dry | |
| 1538 MPa @Temperature 71.0 °C |
223100 psi @Temperature 160 °F |
Dry | |
| 1682 MPa @Temperature 24.0 °C |
244000 psi @Temperature 75.2 °F |
Dry | |
| 1724 MPa @Temperature -59.0 °C |
250000 psi @Temperature -74.2 °F |
Dry | |
| Compressive Modulus | 110.3 GPa @Temperature 24.0 °C |
16000 ksi @Temperature 75.2 °F |
Dry |
| 114.5 GPa @Temperature -59.0 °C |
16610 ksi @Temperature -74.2 °F |
Dry | |
| 114.5 GPa @Temperature 93.0 °C |
16610 ksi @Temperature 199 °F |
Dry | |
| 116.5 GPa @Temperature 71.0 °C |
16900 ksi @Temperature 160 °F |
Dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cured Thickness per Ply (cm) | 0.015-0.016 | Laminate |
| Dry Resin Content (%) | 36-40 | Prepreg |
| Fiber Volume (%) | 50-55 | Laminate |
| Flow (%) | 13-25 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE G 7455 X
- MV Labs LA200 LaBr3·xH2O Lanthanum bromide hydrate
- PolyOne Geon™ L4605 Ivory 3098 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
- Styron Pulse® B250 ABS + Polycarbonate
- Styron XZ 97224.00 Carboxylated SB
- Sax Polymers SAXAMID 126F4MW4 Nylon 6, 40% Glass Fiber and Mineral Reinforced
- A. Schulman PAPERMATCH® T-4448/50 Specialty Masterbatch
- ExxonMobil PP7855E1 Polypropylene Homopolymer
- Azoty Tarnow™ Alphalon™ 32 Nylon 6
- Beijing Evergrow Resources ER-WY-85G Polypropylene Super-Fine Filter Material
Copyright © lookpolymers.com All Rights Reserved