- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyethylene (PE)
- LDPE
- Low Density Polyethylene (LDPE), Molded
- ExxonMobil LD 509.48 Compounding Resin (discontinued **)
ExxonMobil LD 509.48 Compounding Resin (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD 509.48 Compounding Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LD 509.48 is a high melt index homopolymer resin designed to provide good processability in compounding applications.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.913 g/cc | 0.0330 lb/in³ | ExxonMobil Method |
| Melt Flow | 70 g/10 min | 70 g/10 min | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 48 | 48 | 15s; ASTM D2240 |
| Tensile Strength at Break | 7.58 MPa | 1100 psi | ASTM D638 |
| Tensile Strength, Yield | 8.96 MPa | 1300 psi | at 2% Offset; ASTM D638 |
| Film Elongation at Break, MD | 220 % | 220 % | ASTM D882 |
| 1% Secant Modulus | 1450 MPa | 210000 psi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 104 °C | 219 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 76.1 °C | 169 °F | ASTM D1525 |
| Brittleness Temperature | -43.9 °C | -47.0 °F | ASTM D746 |
Users viewing this material also viewed the following:
- Oxford Polymers 604-I Polycarbonate/Polybutylene Terephthalate (PBT) Alloy
- PolyOne Bergadur™ PB40 G30 UF UV Polybutylene Terephthalate (PBT)
- Minelco MagnaDense 4 Fine Aggregate
- Momentive Performance Materials Siloprenâ„¢ FFSL 7061 Fully Fluorinated Liquid Silicone Rubber
- Techmer ES HiFill® PA6 GF50 L 50% Glass Filled (Dry)
- Techmer ES Plastiblend® PC/ABS 1110
- Total PPR 6523WZ Polypropylene, Nucleated Random Copolymer for Injection Molding
- Clariant Renol 66G33 2% Moly Nylon 66, 33% Glass Fiber Reinforced, 2% Molybdenum Disulfide Lubricated
- Arlon LW5015Rxx-P0 0.050" (1.27 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
Copyright © lookpolymers.com All Rights Reserved