SABIC Innovative Plastics LNP THERMOTUF VX99810 Super Tough Nylon
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF VX99810 Super Tough Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Super Tough Nylon, Proprietary Filler(s),
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| 1.177 g/cc | 0.04252 lb/in³ | ASTM D792 | |
| Moisture Absorption | 1.20 % | 1.20 % | 50% RH, 24 hrs; ASTM D570 |
| 1.90 % | 1.90 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D638 |
| 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | 5 mm/min; ISO 527 |
| 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.1 % | 3.1 % | 5 mm/min; ISO 527 |
| 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.41 GPa | 640 ksi | 1 mm/min; ISO 527 |
| 4.66 GPa | 676 ksi | 50 mm/min; ASTM D638 | |
| Flexural Modulus | 3.09 GPa | 448 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.24 GPa | 470 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.43 J/cm | 2.68 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.09 J/cm | 13.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 184 °C | 363 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 75 OG General Purpose Acrylic Resin
- SABIC Innovative Plastics Lexan® HFD1034 PC Copolymer
- Techmer ES Electrablend® PA12 CB
- Tisan TISOPLEN® 10% Talc Filled Heat Stabilized Homopolymer Polypropylene
- A. Schulman ComAlloy® E-13086 Glass/TFE Reinforced PPS
- Goodfellow Titanium 84/Molybdenum 16 Alloy
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Mistron Vapor Filler
- ELASTO UK Dryflex® 650450 TPE, Improved Compression Set and High Temperature Resistance, 45A Hardness
- Addiplast Addilene PMD 50284 Polypropylene Copolymer
- ThyssenKrupp TBL PLUS Structural Steel
Copyright © lookpolymers.com All Rights Reserved