SABIC Innovative Plastics LNP THERMOTUF MF004AI PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF MF004AI PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* MF004AI is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ASTM D955 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ASTM D955 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
| 39.0 MPa | 5660 psi | ASTM D638 | |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527 |
| 4.8 % | 4.8 % | ASTM D638 | |
| Tensile Modulus | 4.82 GPa | 699 ksi | 50 mm/min; ASTM D638 |
| 4.94 GPa | 716 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 41.0 MPa | 5950 psi | ASTM D790 |
| 46.0 MPa | 6670 psi | ISO 178 | |
| Flexural Modulus | 2.75 GPa | 399 ksi | ASTM D790 |
| 3.00 GPa | 435 ksi | ISO 178 | |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.37 J/cm | 8.19 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 106 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 150 °C @Thickness 3.20 mm |
302 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFlex™ GTPE-2272 TPE Compound
- Nilit FRIANYL A63 N-S20 Nylon 6.6 for injection molding
- Phillips 66 COPYLENE® CR120CL-01 Polypropylene, Random Copolymer, Clarified
- Mearthane Durethaneâ„¢ S DS-555D Solid Polyurethane Elastomer
- Struktol POLYDIS 3615 Elastomer modified epoxy prepolymer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N774 Filler
- Chosun Refractories H-1 High Alumina brick
- 3M Nextel™ AF-20 Industrial Woven Fabric 312
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 13% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved