Aclo Accutech Polypropylene Copolymer CP0436M30L Mica Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436M30L Mica Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 30 | 30 | ASTM D785 |
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 2.699 GPa | 391.5 ksi | ASTM D638 |
| Flexural Strength | 31.0 MPa | 4500 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F |
Users viewing this material also viewed the following:
- Kingfa PBT-RG301 Flame Retardant, 30% Glass Fiber Reinforced PBT
- LG Chemical SEETEC H7630 Polypropylene, Homopolymer
- Techmer ES Electrablend® PA6/6 C10 BK 10% Carbon Filled
- Solvay Specialty Polymers Amodel® A-8940 HS Polyphthalamide (PPA), 40% Glass Fiber
- Stir SpA SR 80 2 (PVC)
- A. Schulman POLYBATCH™ Canyon 10277U/4 Concentrate Based In LLDPE
- Channel Industries 5600 Lead Zirconate Titanate Piezoelectric
- Beijing Ranger Chem PBT-201-G20 Flame Retarding FR PBT
- ExxonMobil Escorene® LL-3003 LLDPE/Hexene Premium Cast Stretch Film Resin (discontinued **)
- Toyobo Diaflora® FS 0550B
Copyright © lookpolymers.com All Rights Reserved