Radici Heraform® R 1300 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Radici Group Plastics |
| Trade Name | Heraform® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Radici Heraform® R 1300 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy flowing grade for injection molding of thin-walled parts with high mechanical properties.Information provided by Radici group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 |
| Water Absorption | 0.65 % | 0.65 % | ISO 62 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ISO 527 |
| Elongation at Break | 20 % | 20 % | ISO 527 |
| Tensile Modulus | 2.90 GPa | 421 ksi | ISO 527 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 166 °C | 331 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | ISO 75 |
| Vicat Softening Point | 151 °C @Load 5.10 kg |
304 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
|
| Shrinkage | 1.8 % @Pressure 100 MPa, Temperature 90.0 °C |
1.8 % @Pressure 14500 psi, Temperature 194 °F |
3 mm |
Users viewing this material also viewed the following:
- Momentive Performance Materials LVG342 Low Volatile Silicone Adhesive, Mixed, White
- Solvay TECHNYL® CR 218 V33 Black 21 N Nylon 6, 30% glass fiber, DRY
- Styron CALIBREâ„¢ MEGARAD 2081-15 Polycarbonate Resin
- Total Lumicene® mPE M 5220 High Density Polyethylene, Blow Molding
- A. Schulman POLYBATCH™ Bright Pink 50379 Concentrate Based In Polyethylene
- A. Schulman FORMION™ FI 233 15% Mineral Reinforced Ionomer / Nylon Alloy
- Asahi Kasei Tenac® 4013A Homopolymer Acetal Resin
- 3M RJS-5 3/C Phase Rejacketing System
- Axiall 7801 Rigid PVC, Extrusion, White, High Impact Profile
Copyright © lookpolymers.com All Rights Reserved