SABIC Innovative Plastics LNP THERMOCOMP WF002 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WF002 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* WF002 is a compound based on PBT containing 10% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 |
| 77.0 MPa | 11200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 |
| 77.0 MPa | 11200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.02 GPa | 728 ksi | 1 mm/min; ISO 527 |
| 5.03 GPa | 730 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 121 MPa | 17500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 135 MPa | 19600 psi | ISO 178 | |
| Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.31 GPa | 625 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.36 GPa | 632 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.29 J/cm | 4.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
2.78 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 10.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
5.56 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 179 °C @Thickness 3.20 mm |
354 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nilit Nilamid A3 H G4 General Purpose 20% Glass Reinforced PA66
- Polykemi AB POLYten HDPE S801 HDPE, Good Abrasion Resistance, Excellent Sliding Properties
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Polyfil HG90 Filler
- Kazanorgsintez Oxygen Gaseous, Technical and Medical
- Lanxess Pocan® BF 4215 000000 PBT, 12% Glass Fiber
- Karina 801-10/88-CR White PVC Compound
- SABIC Innovative Plastics LNP Thermocomp MX05038 PP (Europe-Africa-Middle East)
- Entec Hylex® P1010L2 HB Polycarbonate
- BASF Ultramid® B3WGM24 BK30564 10/20% Glass/Mineral Filled PA6 (Dry)
- LNP ULTEM® SMU5852 Polyetherimide, 30% Carbon Fiber Reinforcement, 15% PTFE Lubricant (discontinued **)
Copyright © lookpolymers.com All Rights Reserved