Styron INSPIREâ„¢ DTF8000 ES Compounded Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Styron |
| Trade Name | INSPIRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron INSPIREâ„¢ DTF8000 ES Compounded Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: INSPIREâ„¢ TF 8000 ES is a superior scratch and mar resistant low gloss talc filled interior grad TPO exhibiting excellent low temperature ductility, high modulus and heat performance.Main Characteristics:Interior grade TPOTalc filledHigh modulusLow temperature ductilityScratch and mar resistantMolded in color and accent paint capableInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ISO 527-2/50 |
| Flexural Modulus | 2.22 GPa | 322 ksi | 2.0 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.80 kJ/m² @Temperature -30.0 °C |
1.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 28.0 kJ/m² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Dart Drop, Total Energy | 21.6 J @Thickness 3.20 mm, Temperature 23.0 °C |
15.9 ft-lb @Thickness 0.126 in, Temperature 73.4 °F |
6.7 m/sec, Fully Ductile; ASTM D3763 |
| 28.4 J @Thickness 3.20 mm, Temperature 0.000 °C |
20.9 ft-lb @Thickness 0.126 in, Temperature 32.0 °F |
6.7 m/sec, Fully Ductile; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ISO 75-2/Bf |
| Flame Spread | 30.0 mm/min | 1.18 in/min | Average Extent of Burring; ISO 3795 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Five Finger Scratch | 15 N | FLTM BM108-13 |
| Scratch Resistance - Instrumented | 26 N | Textured, ASTM D7027-05 |
| 31 N | Smooth, 'ASTM D7027-05 |
Users viewing this material also viewed the following:
- Multibase TPSiV® 4200-50A Thermoplastic Elastomer
- SABIC Innovative Plastics Cycoloy® EFX810ME PC
- DuPont Performance Polymers Crastin® SC164 NC010 PBT (Unverified Data**)
- DSM Akulon® K230-HXG6 Nylon 6-30% Glass Reinforced (European Grade) (Dry) (discontinued **)
- Plenco 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
- Hyosung Topilene C600M2 PP
- Fainplast Compounds GS 7080 Flexible PVC, Injection Molding for Technical Items
- 3M Scotch® 3073 Recycled Corrugated Tape
- ExxonMobil Santoprene® 191-85PA12 Thermoplastic Vulcanizate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved