SABIC Innovative Plastics LNP THERMOCOMP RF005 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF005 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF005 is a compound based on Nylon 66 resin containing 25% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 132 MPa | 19100 psi | ASTM D638 |
| 139 MPa | 20200 psi | ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 8.30 GPa | 1200 ksi | 1 mm/min; ISO 527 |
| 9.10 GPa | 1320 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| 205 MPa | 29700 psi | ISO 178 | |
| Flexural Modulus | 7.23 GPa | 1050 ksi | ASTM D790 |
| 8.30 GPa | 1200 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 245 °C @Thickness 3.20 mm |
473 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs PD440 (NH4)2PdCl4 Ammonium tetrachloropalladate(II)
- Johnson Matthey Mattiflux 101 Brazing Flux Powder
- Techmer ES Luriblend® PA6/6 GF10 TL10 10% Glass Filled
- Teknor Apex Elexar® EL 8313 Thermoplastic Elastomer
- Universal Wire Works C355.0 (AMS 4245) Aluminum Alloy Filler Metal
- Lubrizol Estane® ALR CL87A Thermoplastic Polyurethane
- DSM Akulon® K224-G8 PA6-GF40
- Arlon 0.027" (0.6858 mm) Flexible Heater Silicone with Fiberglass Substrate (56586R028)
- A. Schulman ComAlloy Hiloy® 132 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled
- NOVA Chemicals Sclair® 2111 LLDPE Injection Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved