SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing 40% Glass Bead.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 | |
| Moisture Absorption | 1.20 % | 1.20 % | 50% RH, 24 hrs; ASTM D570 |
| 1.55 % | 1.55 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.018 - 0.020 cm/cm @Time 86400 sec |
0.018 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.018 - 0.020 cm/cm @Time 86400 sec |
0.018 - 0.020 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.019 - 0.021 cm/cm @Time 86400 sec |
0.019 - 0.021 in/in @Time 24.0 hour |
ASTM D955 |
| 0.019 - 0.021 cm/cm @Time 86400 sec |
0.019 - 0.021 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ASTM D638 |
| 58.0 MPa | 8410 psi | ISO 527 | |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 |
| 3.3 % | 3.3 % | ASTM D638 | |
| Tensile Modulus | 5.10 GPa | 740 ksi | 50 mm/min; ASTM D638 |
| 5.43 GPa | 788 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 102 MPa | 14800 psi | ASTM D790 |
| 103 MPa | 14900 psi | ISO 178 | |
| Flexural Modulus | 3.78 GPa | 548 ksi | ASTM D790 |
| 4.06 GPa | 589 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.29 J/cm | 4.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J | 2.95 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 49.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 56.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Edistir N 1840 Polystyrene
- Quadrant EPP TIVAR® Cleanstat PE-UHMW + specific additives (ISO Data)
- Total Lacqtene® FD 0270 LDPE, blown film, compounding, injection molding (discontinued **)
- Schmolz + Bickenbach UGICHROM 4305 Austenitic Chrome Plated Bar
- ExxonMobil Spartan EP 150
- Westlake EM184AA Low Density Polyethylene
- Covestro Bayfol® DF-A 1-2 900296 Polycarbonate + ABS
- Braskem TS9022 Blown Film Extrusion Low Density Polyethylene
- A. Schulman ComAlloy Hiloy® 102 Polypropylene, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved