Tra-Con Tra-Bond F114 Optically Clear, Low Viscosity Blush-Free Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy
Manufacturer Tra-Con, Inc.
Trade Name Tra-Bond
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tra-Con Tra-Bond F114 Optically Clear, Low Viscosity Blush-Free Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRA-BOND F114 is a clear, low viscosity, room temperature cure, epoxy system with good optical properties that contains no solvents, has excellent wicking and wetting characteristics, and adheres strongly to glass, ceramics, most metals and plastics. The combination of low viscosity, blush-free cure under high humidity conditions, plus clarity and high spectral transmittance, recommends it for fiber optic (glass and plastic) assembly and repair applications and other high performance electronic and aerospace applications that include structural laminating, lens and prism assembly, and small volume optical potting. Fully cured TRA-BOND F114 provides excellent resistance to salt solutions, mild acids and alkalis and many other chemicals including petroleum solvents, lubricating oils and alcohol. Please Note: This material may have a blue tint in large masses, or thick films. Information provided by Tra-Con Inc.
Physical Properties Metric English Comments
Specific Gravity 1.00 g/cc
1.00 g/cc
Mixed
Solids Content 100 %
100 %
Reactive Solids Content
Volatile Organic Compounds (VOC) Content 9.03 g/l
9.03 g/l
Water Absorption 0.010 %
0.010 %
After 24 hours
Viscosity 625 cP

@Temperature 25.0 °C
625 cP

@Temperature 77.0 °F
After mixing
Mechanical Properties Metric English Comments
Hardness, Shore D 83
83
Adhesive Bond Strength 17.9 MPa
2600 psi
Lap shear, alum to alum, 4 hrs @ 65°C
20.7 MPa
3000 psi
Lap shear, alum to alum, 24 hrs @ 25°C
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 20.0 °C
44.4 µin/in-°F

@Temperature 68.0 °F
Maximum Service Temperature, Air 130 °C
266 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Glass Transition Temp, Tg 53.0 °C
127 °F
Ultimate Tg
Optical Properties Metric English Comments
Refractive Index 1.53
1.53
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+13 ohm-cm
6.00e+13 ohm-cm
Processing Properties Metric English Comments
Cure Time 240 min

@Temperature 65.0 °C
4.00 hour

@Temperature 149 °F
1440 min

@Temperature 25.0 °C
24.0 hour

@Temperature 77.0 °F
Pot Life 35 min
35 min
100 grams
40 min
40 min
25 grams
Descriptive Properties Value Comments
Color Transparent, Clear
Cytotoxicity Study Passes
ISO 10933-5, elution method
Mix Ratio, parts by weight 100/50
Resin/Hardener
Thixotropic Index 1
Working Life hours 1
25 grams
Working Life minutes 35
100 grams