SABIC Innovative Plastics LNP THERMOCOMP NF001 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP NF001 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* NF001 is a compound based on PC+ABS resin containing 5% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 5.3 % | 5.3 % | 5 mm/min; ISO 527 |
| 6.2 % | 6.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.4 % | 3.4 % | Type I, 5 mm/min; ASTM D638 |
| 3.4 % | 3.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1 mm/min; ISO 527 |
| 3.47 GPa | 503 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 94.0 MPa | 13600 psi | ISO 178 |
| Flexural Yield Strength | 102 MPa | 14800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.12 GPa | 453 ksi | 2 mm/min; ISO 178 |
| 3.22 GPa | 467 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.52 J/cm | 2.85 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.05 J/cm | 11.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 34.0 J @Temperature 23.0 °C |
25.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 21.0 J | 15.5 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 82.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
45.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Permabond TA4310 Toughened Acrylic Adhesive
- Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
- SABIC Innovative Plastics NORYL GTX RNX130 PPE+PS+PA
- Lubrizol Isoplast® 2510 Engineering Thermoplastic Polyurethane Resin
- Hexcel® HexForce™ 613 Carbon Fabric
- EMS-Griltech Grilamid® DM 10 Nylon 12 Monofilament
- China-Yixing Longly Refractories Shelf Corundum-Mullite
- Aclo Accutech Polypropylene Copolymer HP0334W30L Wollastonite Reinforced
- Zhejiang Juner PC/PET Alloy
- SABIC Innovative Plastics LNP THERMOCOMP PFB91S PA 6
Copyright © lookpolymers.com All Rights Reserved