PolyOne Edgetek® XP9242701 Polyphenylene Sulfide (PPS)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® XP9242701 Polyphenylene Sulfide (PPS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection Speed: 50 to 80% Holding Time: 3 to 9 sec Injection Time: 1 to 3 sec Cycle Time: 18 to 70 secInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 258 MPa | 37400 psi | ASTM D638 |
| Flexural Modulus | 18.0 GPa | 2610 ksi | ASTM D790 |
| Charpy Impact, Notched | 60.0 J/cm² | 286 ft-lb/in² | J/m; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Middle Barrel Temperature | 290 - 330 °C | 554 - 626 °F | |
| Front Barrel Temperature | 290 - 330 °C | 554 - 626 °F | |
| Nozzle Temperature | 280 - 320 °C | 536 - 608 °F | |
| Mold Temperature | 120 - 150 °C | 248 - 302 °F | |
| Drying Temperature | 130 - 150 °C | 266 - 302 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi | |
| Hold Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi | |
| Back Pressure | 1.00 - 2.50 MPa | 145 - 363 psi | |
| Screw Speed | 80 - 120 rpm | 80 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Carbon Fiber Reinforcement, 10% Filler by Weight | |
| Glass Fiber Reinforcement, 30% Filler by Weight | ||
| Forms | Pellets | |
| Generic Material | PPS | |
| Generic Name | Polyphenylene Sulfide (PPS) | |
| Processing Method | Injection Molding | |
| Regional Availability | Asia Pacific |
Users viewing this material also viewed the following:
- Microcell Composite Company CELLOMER® 6000 SBS Rubber Pellets
- LATI Latene® 7H2-V2HF PP Homopolymer, Heat Stabilized, Flame Retardant
- Solvay MACKERNIUM® KP Surfactant
- Supreme Petrochem SC 203 LV General Purpose Polystyrene
- Teknor Apex Monprene® MP-2970 Thermoplastic Elastomer
- Wellman Wellamid® GS40-60 42LH-N 40% Glass Sphere Filled Nylon 6, Lubricated & Heat Stabilized
- UBE UBESTA® 3030U Nylon 12 (After Sulfuric Acid (10%) for 500 hours)
- BASF Ultramid® 8253 HS BK-102 PA6 (Dry)
- BASF Capron® 8332G Impact Modified, 25% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Asahi Kasei Thermylon® LSG-440A-H 60% Ceramic and Glass Fiber Reinforced, Heat
Copyright © lookpolymers.com All Rights Reserved