SABIC Innovative Plastics LNP THERMOCOMP DX11354 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX11354 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a PC compound with good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0065 cm/cm @Time 86400 sec |
0.0060 - 0.0065 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0065 cm/cm @Time 86400 sec |
0.0060 - 0.0065 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 64 % | 64 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.7 % | 5.7 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.56 GPa | 371 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 7.50 J/cm | 14.1 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.600 mm |
HB @Thickness 0.0236 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.92 @Frequency 1.00e+9 Hz |
2.92 @Frequency 1.00e+9 Hz |
IEC 60250 |
| Dissipation Factor | 0.0070 @Frequency 1.00e+9 Hz |
0.0070 @Frequency 1.00e+9 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP STAT-KON DD0009XP PC
- UBE J2522 Polyethylene
- Borealis SuperCOPO™ LH4201R Polyethylene Insulation Compound, Crosslinkable
- Wanhua Chemical Wanthane® WHT-1685AD Polyester Based TPU
- Asahi Kasei Thermylon® NSG-240A-C 50% Ceramic and Glass Fiber Reinforced
- 3M Scotchcal™ ElectroCut™ 7725-130 Graphic Film
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N339 Filler
- Karina 800-36/395-CY-RT Brown PVC Compound
- MF-5040 Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved