Lehmann & Voss LUVOCOM® 1115/XCF/40 PEK, with carbon fiber
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1115/XCF/40 PEK, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 320 MPa | 46400 psi | |
| Elongation at Yield | 1.2 % | 1.2 % | |
| 1.8 % | 1.8 % | flexural | |
| Modulus of Elasticity | 40.0 GPa | 5800 ksi | |
| Flexural Strength | 465 MPa | 67400 psi | |
| Flexural Modulus | 35.0 GPa | 5080 ksi | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| 300 °C | 572 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 330 °C | 626 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 390 - 420 °C | 734 - 788 °F | |
| Zone 1 | 370 - 390 °C | 698 - 734 °F | |
| Zone 2 | 380 - 420 °C | 716 - 788 °F | |
| Zone 3 | 390 - 420 °C | 734 - 788 °F | |
| Mold Temperature | 180 - 230 °C | 356 - 446 °F | |
| Drying Temperature | 140 °C @Time 14400 - 21600 sec |
284 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| 150 °C @Time 14400 - 28800 sec |
302 °F @Time 4.00 - 8.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Lanxess Pocan® C 1202 000000 PET + PC
- Solvay Specialty Polymers Ixef® HC-1022 Polyarylamide (PARA), 50% Glass Fiber (Conditioned)
- SABIC Innovative Plastics LNP THERMOCOMP EXTC8143 PC (Asia Pacific)
- Styrolution Novodur® 450 ABS
- A. Schulman POLYBATCH™ Blue 40567 Concentrate Based In LDPE
- Master Bond EP42HT-2 Epoxy Adhesive Resists Sterilization
- Diamond Polymers ASA S124 ASA Weatherable Polymers Injection Molding Grade, Medium Modulus