SABIC Innovative Plastics LNP THERMOCOMP AX06437 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AX06437 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* AX06437 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | color; ASTM D792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| 1.175 g/cc | 0.04245 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.220 % | 0.220 % | 50% RH, 24 hrs; ASTM D570 |
| 0.320 % | 0.320 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527 |
| 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO 527 |
| 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.9 % | 6.9 % | Type I, 5 mm/min; ASTM D638 |
| 7.5 % | 7.5 % | ISO 527 | |
| 64.1 % | 64.1 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| 1.9 % | 1.9 % | ISO 527 | |
| Tensile Modulus | 3.18 GPa | 461 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| 92.0 MPa | 13300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.01 GPa | 437 ksi | ISO 178 |
| 3.06 GPa | 444 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.88 J/cm | 5.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*3; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*3; ISO 180/1U |
| 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.4 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 91.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.75 @Frequency 1.00e+9 Hz |
2.75 @Frequency 1.00e+9 Hz |
ASTM D150 |
| Dissipation Factor | 0.0024 @Frequency 1.00e+9 Hz |
0.0024 @Frequency 1.00e+9 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Polymer Resources PPX/NY G20 PPO/Nylon 66 Alloy , 20% Glass Reinforced
- Magyar Aluminum ALO-P90-20 Alumina
- Lehmann & Voss LUVOCOM® 1/CF/15/TF/20/BK Polyamide 66, with carbon fiber and PTFE
- Ineos ABS Triax® KU2-3154 ABS + Nylon 6
- Techmer ES HiFill® PA6/6 GF/M35 HS BK 35% Glass/Mineral Fiber Filled
- Dow Corning SYL-OFF® PMCPSL 9156 Release Modifier
- Overview of materials for Phenolic, Novolac, Mineral/Cellulose Filled
- Polyram RamTough PZ304G2 Polycarbonate, 10% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved