SABIC Innovative Plastics LNP THERMOCOMP 9X10312 PA (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 9X10312 PA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
9X10312 is 50% glass fiber reinforced, impact modified nylon material. High modulus, high flow and good ductility, Low Moisture Absorption.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.80 % | 0.80 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0012 cm/cm @Thickness 3.20 mm |
0.0012 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 15 g/10 min @Load 2.16 kg, Temperature 300 °C |
15 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 212 MPa | 30700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 310 MPa | 45000 psi | ASTM D790 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
| Izod Impact, Notched | 1.50 J/cm | 2.81 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.0 @Frequency 1.00e+9 Hz |
4.0 @Frequency 1.00e+9 Hz |
ASTM ES 7-83 |
| Dissipation Factor | 0.010 @Frequency 1.10e+9 Hz |
0.010 @Frequency 1.10e+9 Hz |
ASTM ES 7-83 |
Users viewing this material also viewed the following:
- RheTech Products GC30P200-01BG 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, General Purpose Black, Blow Molding Grade
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)
- Ravago Manufacturing Americas Hylac® FR134 ABS
- Chevron Phillips K-Resin® KR01BR SBC (discontinued **)
- Fiberfil® PP-60/CC/40 Polypropylene Homopolymer, 40% Calcium Carbonate
- Silberline Silvet® 950-20-P
- Cossa Polimeri ESTACARB 0820 GF V0-5V HF Flame Retardant Polycarbonate
- DuPont Performance Polymers Crastin® SK603 BK851 Polybutylene Terephthalate (PBT) (Unverified Data**)
- 3M 2552/Silver Damping Foils
- Aclo Accuguard Polypropylene HP0362V0CSL Homopolymer Flame Retardant Copper Stabilized
Copyright © lookpolymers.com All Rights Reserved