- Nilit FRIANYL B63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced
Nilit FRIANYL B63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, good conductive and electrostatic properties.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.4 % | 1.5 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0040 - 0.012 cm/cm | 0.0040 - 0.012 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 182 MPa | 26400 psi | ISO 2039-1 |
| Tensile Strength at Break | 200 MPa | 29000 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527 |
| Charpy Impact Unnotched | 2.30 J/cm² | 10.9 ft-lb/in² | DIN 53453 |
| 3.80 J/cm² | 18.1 ft-lb/in² | ISO 179/1eU | |
| 2.10 J/cm² @Temperature -40.0 °C |
9.99 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 4.30 J/cm² @Temperature -30.0 °C |
20.5 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DIN 53453 |
| 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA | |
| 0.500 J/cm² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 150 ohm-cm | 150 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
Users viewing this material also viewed the following:
- Osprey Metals 49FeCo2V Cobalt Alloy Powder (Grade 95% - 16)
- PEAK Werkstoff DISPAL S690 Aluminum Alloy, AlCu4MgAg, Condition T4
- Abatron AboCast 8102-1/AboCure 8102-1 Epoxy (discontinued **)
- Iran Petrochemical (PCC) 60505 High Density Polyethylene
- SSAB Tunnplat Docol® DC04 (Fe P04) Deep-drawing Steel
- China Tungsten YMo55.0-B MoO3, Lump Standard
- Dow Corning 3-4118 GEL A&B
- BASF Novolen® 2900 H Polypropylene
- Cheng Yu Plastic FV30720 POM, 20% Mineral Reinforced
- 3M P591 Plastic Primer
Copyright © lookpolymers.com All Rights Reserved