Samsung Cheil Industries Infino® HM-3301GL PC, Glass Filled High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HM-3301GL PC, Glass Filled High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC/GF material that is used for electric and electronic partsInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength at Break | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 118 MPa | 17100 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 6.37 GPa | 925 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 7.35 GPa | 1070 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 6.35 mm |
2.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.57 J/cm @Thickness 3.17 mm |
2.94 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C @Thickness 6.40 mm |
295 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C @Thickness 6.40 mm |
277 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | B/50; ISO R306 |
| 151 °C | 304 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
|
| V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
||
| V-0 @Thickness 3.00 - 6.00 mm |
V-0 @Thickness 0.118 - 0.236 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
STM D150 |
| Dissipation Factor | 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
STM D150 |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® HB-W952-A HDPE Extrusion Resin
- PolyOne Geon™ 170 Series L100UF Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Covestro Apec® 2000 Polycarbonate (discontinued **)
- DSM Akulon® S223-PG2U (Dry) 13% Glass Reinforced, Impact Modified Nylon 66 (North America) (discontinued **)&
- Overview of materials for Phenolic, Novolac, Mineral/Flock Filled
- I. Stern N2560 General Purpose Crystal Polystyrene
- SABIC Innovative Plastics LNP LUBRICOMP RFL16 PA 66 (Asia Pacific)
- Arlon 55173R045 0.045" (1.14 mm) Cured Silicone Rubber with Fiberglass Substrate
- RheTech Products CC20P200-01 20% Calcium Carbonate Reinforced Polypropylene Copolymer, Black
Copyright © lookpolymers.com All Rights Reserved