SABIC Innovative Plastics LNP Stat-kon WFD059 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon WFD059 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* WFD059 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| 1.61 g/cc | 0.0582 lb/in³ | ASTM D 792 | |
| Linear Mold Shrinkage, Flow | 0.0056 cm/cm @Time 86400 sec |
0.0056 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D 638 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ASTM D 638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D 638 |
| Elongation at Yield | 1.5 % | 1.5 % | ASTM D 638 |
| Tensile Modulus | 8.96 GPa | 1300 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D 790 |
| 135 MPa | 19600 psi | ISO 178 | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
| 8.27 GPa | 1200 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.73 J/cm @Temperature 23.0 °C |
6.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 ohm - 1e+05 | 1000 ohm - 1e+05 | ASTM D 257 |
Users viewing this material also viewed the following:
- Outokumpu 353MA® High Temperature Austenitic Stainless Steel
- Polymer Resources PC/ABS-GP1-[color]-UV General Purpose PC/ABS Alloy, UV-stabilized
- Huntsman Araldite GY 509 Bisphenol A Epoxy Liquid Resin
- Lord Adhesives 26 No-Mix Accelerator for 200/500 Series
- SABIC Innovative Plastics LNP THERMOCOMP RF008 PA 66 (Asia Pacific)
- SABIC Innovative Plastics LNP STAT-KON RE008 PA 66
- A. Schulman POLYBATCH™ Blue 40343/4 Concentrate Based In Polyethylene
- Addiplast Addinyl A2 V15 Nylon 66, 15% Glass Filled
- AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition C
- LATI Latimass 62-05 D040 PA6
Copyright © lookpolymers.com All Rights Reserved