- Polybutylene Terephthalate (PBT), Unreinforced, Molded
- Polybutylene Terephthalate (PBT), Extrusion Grade
- Lanxess Pocan® DP 1105 000000 PBT
Lanxess Pocan® DP 1105 000000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® DP 1105 000000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, injection molding, extrusion, improved flowability
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 % | 0.50 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0022 cm/cm | 0.0022 in/in | ISO 294-4, 2577 |
| Melt Flow | 55 g/10 min @Load 1.20 kg, Temperature 250 °C |
55 g/10 min @Load 2.65 lb, Temperature 482 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
| Elongation at Break | 10 % | 10 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 13.5 J/cm² @Temperature 23.0 °C |
64.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Impact | 2896 | 2896 | Puncture maximum force (N); ISO 6603-2 |
| 1072 @Temperature -30.0 °C |
1072 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 14.7 J | 10.8 ft-lb | ISO 6603-2 |
| 2.00 J @Temperature -30.0 °C |
1.48 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 180 °C | 356 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC 60695-11-10 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 | |
| Oxygen Index | 25.1 % | 25.1 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 30.2 kV/mm | 767 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0014 @Frequency 100 Hz |
0.0014 @Frequency 100 Hz |
IEC 60250 |
| 0.0224 @Frequency 1.00e+6 Hz |
0.0224 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 350 V | 350 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GHMR,07-030 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- RheTech Products CC30P100-01 30% Calcium Carbonate Reinforced Polypropylene, Black
- Omni Plastics OmniLon™ 6/6 PA6/6 GR33 Glass Reinforced Nylon
- SABIC Innovative Plastics Lexan® FL900P PC (Europe-Africa-Middle East)
- A. Schulman PP 3488-01 Polypropylene Homopolymer Polypropylene
- Goodfellow Nickel 75/Manganese 25 Alloy
- Plastics Group Polifil® GFPC-30 30% Glass-Reinforced Polycarbonate
- ChevronTexaco Gear Compounds EP, ISO 1000
- ExxonMobil HD 6719.62 Injection Molding Resin
- 3M 9499 Splicing Tape
- Aptek DI-STRATE 1500-1 Microwave/RF Foam Substrate
Copyright © lookpolymers.com All Rights Reserved