SABIC Innovative Plastics LNP Stat-kon DX07323 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon DX07323 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DX07323 is a compound based on polycarbonate resin containing conductive fillers. Added features of this compound includes: ESD safe and excellent low-temperature impact performance, intended for compliance to ATEX.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D 792 |
| 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | SABIC Method |
| 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | SABIC Method |
| 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 | |
| Melt Flow | 50 g/10 min @Load 10.0 kg, Temperature 300 °C |
50 g/10 min @Load 22.0 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 55 g/10 min @Load 10.0 kg, Temperature 300 °C |
55 g/10 min @Load 22.0 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | ASTM D 638 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D 638 |
| 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D 638 |
| 9.0 % | 9.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D 638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.40 GPa | 348 ksi | 5 mm/min; ASTM D 638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D 790 |
| 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D 790 |
| 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.00 J/cm @Temperature -40.0 °C |
1.87 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 1.80 J/cm @Temperature 23.0 °C |
3.37 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 15.0 J/cm @Temperature -40.0 °C |
28.1 ft-lb/in @Temperature -40.0 °F |
ASTM D 4812 |
| 16.0 J/cm @Temperature 23.0 °C |
30.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A |
| 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² @Temperature -40.0 °C |
47.6 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1U |
| 130 kJ/m² @Temperature 23.0 °C |
61.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Flammability, UL94 | V-1 @Thickness 2.50 mm |
V-1 @Thickness 0.0984 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+6 - 1.00e+10 ohm-cm | 1.00e+6 - 1.00e+10 ohm-cm | ASTM D 257 |
| Surface Resistance | 1.00e+6 - 1.00e+10 ohm | 1.00e+6 - 1.00e+10 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- PPT LSF180 Low Sintering Temperature Ferrite Powder
- Mitsui Fybrel® Y 600 Polyolefin Synthetic Pulp, Wet Processes (discontinued **)
- PolyOne Edgetek® AS-40GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
- H.C. Starck Amperit® 175.2 Nickel (Ni)
- SABIC Innovative Plastics NORYL WCA875 PPE-TPE (Europe-Africa-Middle East)
- SSAB Tunnplat Docol® 1200 DP High-strength Steel
- Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, Dry As Molded
- MV Labs RH470 [(C6H5)3P]2Rh(CO)Cl Carbonylchlorobis(triphenylphosphine) rhodium(I)
- Assab Steels 7210M Machinery Steel
- Eastman D4042-P Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved