Barlog Plastics KEBATER BF130 PBT, 30% glass fiber reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATER |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATER BF130 PBT, 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT-GF30Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | similar to ISO 62 test |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
UL Registered; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | PBT-GF30 |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 3010-60A Thermoplastic Silicone Vulcanizate
- Rogers Corporation TMM® TMM4 Ceramic Thermoset Polymer Composite
- NOVA Chemicals DYLARK® 250 Impact Grade Engineering Resin
- BASF Capron® 5233G HS BK-102 33% Glass-Filled Nylon 66 (Dry) (discontinued **)
- Shakespeare Isocorâ„¢ CU145SI Nylon 6/66
- Wellman EcoLon® MR1660-BK 40% Mineral Reinforced Post Consumer Compound Nylon 66
- Westlake Hifor LT74113 Hexene Linear Low Density Polyethylene
- Polyram RamOfin PPH300G9 Polypropylene, 45% Glass Fiber
- Cossa Polimeri ESTASTIR GP 1000 Polystyrene
- Chosun Refractories SAL85BR Special High Alumina brick
Copyright © lookpolymers.com All Rights Reserved