Polimeri Europa Clearflex® H&T FGH 196 Hexene Copolymer Linear Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex® H&T
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® H&T FGH 196 Hexene Copolymer Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex H&T FGH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films obtained from Clearflex H&T FGH 196 show excellent optical properties, a wide sealing window, both hot tack and heat seal, together with a low sealing initiation temperature (S.I.T.) and outstanding impact, puncture and Elmendorf tear resistance.Main Applications: Clearflex H&T FGH 196, for its overall characteristics, is the right choice for all applications, like silage stretch film, low thickness high clarity packaging film, requiring a superior mechanical strength. Moreover, the excellent sealability behavior makes it ideal for lamination film production.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.916 g/cc
0.916 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.90 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ISO 527-3
Film Tensile Strength at Yield, TD 9.00 MPa
1310 psi
ISO 527-3
Film Elongation at Break, MD 500 %
500 %
ISO 527-3
Film Elongation at Break, TD 700 %
700 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 16.304 g/micron
414.12 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 26.494 g/micron
672.95 g/mil
ISO 6383-2
Dart Drop Test 390 g
0.860 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ISO 527-3
Film Tensile Strength at Break, TD 35.0 MPa
5080 psi
ISO 527-3
1% Secant Modulus, MD 170 MPa
24700 psi
ISO 527-3
1% Secant Modulus, TD 200 MPa
29000 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 123 °C
253 °F
Internal method
Vicat Softening Point 95.0 °C

@Load 1.00 kg
203 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ISO 14782
Gloss 70 %
70 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified