SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-LOY A3000 is a compound based on Acrylonitrile butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistatic. Also known as: STAT-LOY A
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| 1.065 g/cc | 0.03848 lb/in³ | ASTM D792 | |
| Moisture Absorption | 1.08 % | 1.08 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
| 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527 |
| 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D638 |
| 24.2 % | 24.2 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.01 GPa | 292 ksi | 1 mm/min; ISO 527 |
| 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 65.0 MPa | 9430 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 59.0 MPa | 8560 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.98 GPa | 287 ksi | 2 mm/min; ISO 178 |
| 2.09 GPa | 303 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.82 J/cm | 5.28 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 32.0 J | 23.6 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 93.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 93.4 µm/m-°C @Temperature 23.0 - 60.0 °C |
51.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 101 µm/m-°C @Temperature -40.0 - 40.0 °C |
56.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 101 µm/m-°C @Temperature 23.0 - 60.0 °C |
56.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 - 1.00e+11 ohm | 1.00e+9 - 1.00e+11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ NN-000/10T-2S Black Polyamide 66 (Nylon 66)
- Honeywell Capran® Oxyshield™ M-OPA (0.60 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film
- Magyar Aluminum ALO-G22-10 Alumina
- SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS
- SABIC Innovative Plastics LNP VERTON MV008SU PP
- Lubrizol ESTALOC® T5160 Ether-Type, Reinforced Engineering Thermoplastic (European Grade)
- Eurostar Staramide AG8 PA66, 40% Glass Fiber Reinforced, Injection Molding
- Bapolene® 270F Low Density Polyethylene Film Extrusion Resin
- BYK Cloisite® 15A Nanoclay
- BNZ Materials 2855LI Insulating Aggregate
Copyright © lookpolymers.com All Rights Reserved