SABIC Innovative Plastics LNP STAT-KON FX91304 PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON FX91304 PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* FX91304 is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D792 |
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 |
| 24.0 MPa | 3480 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 5 mm/min; ISO 527 |
| 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.6 % | 3.6 % | Type I, 5 mm/min; ASTM D638 |
| 3.7 % | 3.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.42 GPa | 351 ksi | 1 mm/min; ISO 527 |
| 3.00 GPa | 435 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 36.0 MPa | 5220 psi | ISO 178 |
| Flexural Yield Strength | 35.0 MPa | 5080 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.11 GPa | 306 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.66 J/cm | 3.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.05 J/cm | 9.46 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 232 µm/m-°C @Temperature -30.0 - 30.0 °C |
129 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 6.0 ohm | 2.0 - 6.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nylene® 733 Nylon 6
- LATI Latilub 66-15T K/30 PA66, 30% Carbon Fiber Reinforced, PTFE Filled
- Spartech PP7140 Talc Filled High Impact Copolymer
- A. Schulman PP 3475-01 Polypropylene High Melt Homopolymer Polypropylene
- Toyobo Zylon® HM Fiber/Epoxy Matrix Unidirectional Composite
- Azoty Tarnow™ TARNOFORM 300 GF4 POM
- ExxonMobil Mobil Almo 525
- Hexcel® HexWeb® CFC™-20-1/8-5.0 Composite Flooring Honeycomb Core
Copyright © lookpolymers.com All Rights Reserved