SABIC Innovative Plastics LNP LUBRICOMP DCL33E PC (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DCL33E PC (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* DCL33E is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features include; Internally Lubricated, Electrically Conductive, Easy Molding.

Physical Properties	Metric	English	Comments
Density	1.35 g/cc	0.0488 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0015 - 0.0030 cm/cm	0.0015 - 0.0030 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	121 MPa	17500 psi	5 mm/min; ISO 527
Elongation at Break	1.8 %	1.8 %	5 mm/min; ISO 527
Flexural Strength	177 MPa	25700 psi	2 mm/min; ISO 178
Flexural Modulus	11.9 GPa	1730 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	25.0 kJ/m²	11.9 ft-lb/in²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	139 °C	282 °F	Flatw 80104 sp=64mm; ISO 75/Af
Flammability, UL94	V-0 @Thickness 4.50 mm	V-0 @Thickness 0.177 in	UL 94

Electrical Properties	Metric	English	Comments
Surface Resistance	100 - 10000 ohm	100 - 10000 ohm	ASTM D257