SABIC Innovative Plastics LNP Lubricomp DL002E PC (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Lubricomp DL002E PC (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* DL002E is a compound based on Polycarbonate resin containing PTFE. Added features include: Internally Lubricated, Easy Molding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.25 g/cc	0.0452 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.0 MPa	7980 psi	5 mm/min; ISO 527
Elongation at Yield	5.3 %	5.3 %	5 mm/min; ISO 527
Tensile Modulus	2.20 GPa	319 ksi	1 mm/min; ISO 527
Flexural Yield Strength	88.0 MPa	12800 psi	2 mm/min; ISO 178
Flexural Modulus	2.10 GPa	305 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	8.00 kJ/m² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	73.0 µm/m-°C @Temperature 23.0 - 60.0 °C	40.6 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	73.0 µm/m-°C @Temperature 23.0 - 60.0 °C	40.6 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	135 °C	275 °F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	123 °C	253 °F	Flatw 80104 sp=64mm; ISO 75/Af