| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY RF203H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* RF203H is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
| 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D638 |
| 3.8 % | 3.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.89 GPa | 709 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 128 MPa | 18600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 140 MPa | 20300 psi | ISO 178 | |
| Flexural Modulus | 4.18 GPa | 606 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.50 GPa | 798 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.830 J/cm | 1.55 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.46 J/cm | 12.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.30 | 0.30 | ASTM D3702 Modified |
| K (wear) Factor | 141 x 10-8 mm³/N-M | 70.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- MV Labs AL900 AlPO4 Aluminum phosphate
- S&E Specialty Polymers GPP™ 1005M-EXLT PP
- Premix Premi-Glas® 1206 LD Fiberglass Reinforced Thermoset SMC
- Hyosung Topilene J642 PP
- SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Asia Pacific)
- Spartech PP5210 Calcium Carbonate Filled Homopolymer
- Solvay ANTAROX® BL 225 Surfactant
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N650 Filler
- DuPont Performance Polymers Kalrez® Spectrum™ 6380 Fluoroelastomer
- Braskem IB58 HDPE Injection Molding Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved