Radici Radilon® ALX14080 (dry) Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Radici Group Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Radici Radilon® ALX14080 (dry) Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Medium high viscosityInformation provided by Radici group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527-1/2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/2 |
| Elongation at Yield | 4.2 % | 4.2 % | ISO 524-1/2 |
| Tensile Modulus | 3.25 GPa | 471 ksi | ISO 527-1/2 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178 |
| Charpy Impact, Notched | 0.670 J/cm² | 3.19 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 1135 7-1-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75/2Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75/2Af |
| Vicat Softening Point | 240 °C | 464 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- Proto3000 ABS-M30 Fused Deposition Modeling Polymer
- PTS Trimid® N66-G13LU 13% Glass Fiber Reinforced Utility Lubricated Nylon 6/6
- Gouda Vuurvast CURON 160 FS Dense Refractory Castable
- Inno-Comp INNOBATCH® PPH 6160 60% Talc-Filled Polypropylene Homopolymer
- Iran Petrochemical (PCC) EX 2 S HF 7750 M2 High Density Polyethylene
- Techmer ES Luriblend® PC IM FR
- Wellman Wellamid® T512-BK 15% Talc/Glass Reinforced, Dimensionally Stable Grade Nylon 6
- ExxonMobil LDPE LD 654 Low Density Polyethylene Resin (European Grade)
- Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure
Copyright © lookpolymers.com All Rights Reserved