LATI Latiohm 80-04 PD01 G/30 PPS, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler
Manufacturer LATI
Trade Name Latiohm
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latiohm 80-04 PD01 G/30 PPS, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semiconductive/dissipative product based on Polyphenylene Sulfide (PPS). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.64 g/cc
0.0592 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0040 cm/cm
0.0025 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0090 cm/cm
0.0065 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
Elongation at Break 0.50 %
0.50 %
Tensile Modulus 22.5 GPa
3260 ksi
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
491 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Surface Resistance 1000 ohm
1000 ohm
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa