BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G HS BK-106. In parts containing cross sections, significant pressure drops are encountered during filling.

Physical Properties	Metric	English	Comments
Density	1.48 g/cc	0.0535 lb/in³	dry; ISO 1183
Water Absorption	0.90 %	0.90 %	24 hour; ISO Test
	5.7 %	5.7 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	1.6 %	1.6 %	beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	38.0 MPa @Temperature 120 °C	5510 psi @Temperature 248 °F	ASTM Test
	38.0 MPa @Temperature 120 °C	5510 psi @Temperature 248 °F	ISO Data
	46.0 MPa @Temperature 80.0 °C	6670 psi @Temperature 176 °F	ISO Data
	46.0 MPa @Temperature 80.0 °C	6670 psi @Temperature 176 °F	ASTM Test
	153 MPa @Temperature -40.0 °C	22200 psi @Temperature -40.0 °F	ASTM Test
	153 MPa @Temperature -40.0 °C	22200 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Ultimate	67.0 MPa	9720 psi	5mm/min; ISO 527
Elongation at Break	5.6 %	5.6 %	5mm/min; ISO 527
	2.6 % @Temperature -40.0 °C	2.6 % @Temperature -40.0 °F	ISO Data
	2.6 % @Temperature -40.0 °C	2.6 % @Temperature -40.0 °F	ASTM Test
	5.9 % @Temperature 80.0 °C	5.9 % @Temperature 176 °F	ISO Data
	5.9 % @Temperature 80.0 °C	5.9 % @Temperature 176 °F	ASTM Test
	7.3 % @Temperature 120 °C	7.3 % @Temperature 248 °F	ASTM Test
	7.3 % @Temperature 120 °C	7.3 % @Temperature 248 °F	ISO Data
Tensile Modulus	3.90 GPa	566 ksi	1mm/min; ISO 527
	2.32 GPa @Temperature 120 °C	336 ksi @Temperature 248 °F	ISO Data
	3.05 GPa @Temperature 80.0 °C	442 ksi @Temperature 176 °F	ISO Data

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Descriptive Properties	Value	Comments
Color	BK-126
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding

Users viewing this material also viewed the following: