SABIC Innovative Plastics LNP LUBRICOMP RBL36L PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RBL36L PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RBL36L is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features s of this grade are: Low Extractable, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.430 % | 0.430 % | 50% RH, 24 hrs; ASTM D570 |
| 0.540 % | 0.540 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
| 66.0 MPa | 9570 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 8.3 % | 8.3 % | 5 mm/min; ISO 527 |
| 9.1 % | 9.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 8.8 % | 8.8 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.10 GPa | 595 ksi | 1 mm/min; ISO 527 |
| 4.18 GPa | 606 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 109 MPa | 15800 psi | ISO 178 |
| Flexural Modulus | 3.81 GPa | 553 ksi | 2 mm/min; ISO 178 |
| 3.95 GPa | 573 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.410 J/cm | 0.768 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.37 J/cm | 6.31 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.57 | 0.57 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.58 | 0.58 | ASTM D3702 Modified |
| K (wear) Factor | 64.5 x 10-8 mm³/N-M | 32.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 102 µm/m-°C @Temperature -30.0 - 30.0 °C |
56.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 75.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 231 °C @Thickness 3.20 mm |
448 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Reliance Industries Polypropylene - Wollastonite filled
- Northstar Polymers MPP-A80E High Performance Polyether
- Kolon KOCETAL® LF301 Wear Modified Acetal Resin
- SABIC Innovative Plastics LNP Thermocomp RFZ42 PA 66
- SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Asia Pacific)
- Techmer ES HiFill FR® PA6 E FR
- SABIC Innovative Plastics LNP THERMOCOMP RC00A PA6.6 (Europe-Africa-Middle East)
- A. Schulman ComAlloy® E-13819 Heat Dissipative PPS
- Hexcel® HexWeb® HRH-36 - 1/8 - 4.5 Para-Aramid/Phenolic Core
Copyright © lookpolymers.com All Rights Reserved