Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1200°F (650°C)

Category	Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer	Special Metals (includes the former Inco Alloys International Inc.)
Trade Name	INCONEL®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1200°F (650°C).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain size 9.5. Other property values are typical of this alloy.Data provided by the manufacturer, Special Metals.

Physical Properties	Metric	English	Comments
Density	8.44 g/cc	0.305 lb/in³

Mechanical Properties	Metric	English
Hardness, Rockwell B	100	100
Tensile Strength, Ultimate	1040 MPa	151000 psi
Tensile Strength, Yield	835.6 MPa @Strain 0.200 %	121200 psi @Strain 0.200 %
Elongation at Break	31 %	31 %
Modulus of Elasticity	208 GPa	30200 ksi
Poissons Ratio	0.28	0.28
Shear Modulus	81.4 GPa	11800 ksi

Thermal Properties	Metric	English	Comments
CTE, linear	12.8 µm/m-°C @Temperature 21.0 - 100 °C	7.11 µin/in-°F @Temperature 69.8 - 212 °F	Mean
	13.3 µm/m-°C @Temperature 21.0 - 300 °C	7.39 µin/in-°F @Temperature 69.8 - 572 °F	Mean
	13.9 µm/m-°C @Temperature 21.0 - 500 °C	7.72 µin/in-°F @Temperature 69.8 - 932 °F	Mean
	14.9 µm/m-°C @Temperature 21.0 - 700 °C	8.28 µin/in-°F @Temperature 69.8 - 1290 °F	Mean
Specific Heat Capacity	0.410 J/g-°C	0.0980 BTU/lb-°F
Thermal Conductivity	9.70 W/m-K	67.3 BTU-in/hr-ft²-°F
Melting Point	1290 - 1350 °C	2350 - 2460 °F
Solidus	1290 °C	2350 °F
Liquidus	1350 °C	2460 °F
Maximum Service Temperature, Air	650 °C	1200 °F	resistance to low cycle and thermal fatigue

Component Elements Properties	Metric	English	Comments
Aluminum, Al	<= 0.40 %	<= 0.40 %
Carbon, C	<= 0.030 %	<= 0.030 %
Chromium, Cr	20 - 23 %	20 - 23 %
Cobalt, Co	<= 1.0 %	<= 1.0 %
Iron, Fe	<= 5.0 %	<= 5.0 %
Manganese, Mn	<= 0.50 %	<= 0.50 %
Molybdenum, Mo	8.0 - 10 %	8.0 - 10 %
Nickel, Ni	>= 58 %	>= 58 %
Niobium, Nb (Columbium, Cb)	3.15 - 4.15 %	3.15 - 4.15 %	Includes Ta
Nitrogen, N	<= 0.020 %	<= 0.020 %
Phosphorous, P	<= 0.015 %	<= 0.015 %
Silicon, Si	<= 0.020 %	<= 0.020 %
Sulfur, S	<= 0.015 %	<= 0.015 %
Titanium, Ti	<= 0.40 %	<= 0.40 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.000132 ohm-cm	0.000132 ohm-cm
Magnetic Permeability	1.0006	1.0006	at 200 Oersted (15.9 kA/m)