Borealis Low Sulfur™ LE0595 Crosslinkable Semiconductive Compound for Shielding of Power Cables
| Category | Polymer , Thermoplastic , Ethylene Vinyl Acetate |
| Manufacturer | Borealis |
| Trade Name | Low Sulfur™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis Low Sulfur™ LE0595 Crosslinkable Semiconductive Compound for Shielding of Power Cables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low Sulphur LE0595 is designed for use as a conductor and bonded insulation shield for medium and high voltage cables. LE0594 is a peroxide crosslinkable compound and is specifically intended to meet cable specifications based on crosslinked polyethylene or EPR insulations. It lends itself readily to various manufacturing processes including triple extrusion. LE0595 is manufactured in Borealis ` plant in Belgium.Low Sulphur LE0595 is based on an ethylene ethyl acrylate copolymer (EEA) and is designed for use a in a conductor shield with copper conductors.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D1928/D 1505 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 11.0 MPa | >= 1600 psi | Heat Aging (168 hrs at 150°C); ASTM D638 |
| 22.1 MPa | 3200 psi | ASTM D638 | |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Tensile Set | >= 100 % | >= 100 % | Retention; ASTM D638 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 25.0 ohm-cm | 25.0 ohm-cm | ASTM D991 |
| 40.0 ohm-cm @Temperature 40.0 °C |
40.0 ohm-cm @Temperature 104 °F |
ASTM D991 | |
| 80.0 ohm-cm @Temperature 60.0 °C |
80.0 ohm-cm @Temperature 140 °F |
ASTM D991 | |
| 325 ohm-cm @Temperature 80.0 °C |
325 ohm-cm @Temperature 176 °F |
ASTM D991 | |
| 400 ohm-cm @Temperature 130 °C |
400 ohm-cm @Temperature 266 °F |
ASTM D991 | |
| 525 ohm-cm @Temperature 100 °C |
525 ohm-cm @Temperature 212 °F |
ASTM D991 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | >= 110 °C | >= 230 °F | |
| Front Barrel Temperature | >= 100 °C | >= 212 °F | |
| Die Temperature | >= 120 °C | >= 248 °F | |
| Head Temperature | >= 120 °C | >= 248 °F |
Users viewing this material also viewed the following:
- M. Holland Company PC406R Polycarbonate
- SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopoly (Asia Pacific)
- Techmer ES HiFill® ABS GF40 40% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP VF008A PA 66
- Styron CALIBREâ„¢ 1060 DVD Polycarbonate Resin
- Borealis Visico™/Ambicat™ ME4425/LE4476 Ambient Curing, Moisture-Crosslinking Polyethylene Compound for Low Voltage Insulation
- ChevronTexaco DIESELMOTIVE® Direct Injector Cleaner, for Heavy Duty Diesel Engines
- Akro-Plastic Akromid® B3 GF 35 (2473) PA 6 Dry, 35% Glass Filled
- Bulk Molding Compounds BMC 695 Vinyl Ester Molding Compound
Copyright © lookpolymers.com All Rights Reserved