ExxonMobil Escorene® LD-722 High EVA Film and Compounding Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD-722 High EVA Film and Compounding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer resin for specialty film and compounding applications. Outstanding heat sealability along with excellent strength properties are key attributes of films made from LD-722.Applications: Heat seal layer in blown and cast coextruded films; Pallet stretch wrap.

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in³	Exxon Method
Environmental Stress Crack Resistance	>= 500 hour	>= 500 hour	F50, Condition A; ASTM D1693
Melt Flow	3.0 g/10 min	3.0 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	80	80	ASTM D2240
Hardness, Shore D	29	29	ASTM D2240
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Flexural Modulus	0.0410 GPa	5.95 ksi	1% Secant, ASTM D790
Tensile Impact Strength	648 kJ/m²	308 ft-lb/in²	23°C; ASTM D-1822

Thermal Properties	Metric	English	Comments
Melting Point	81.0 °C	178 °F	Exxon Method
Vicat Softening Point	57.0 °C	135 °F	1000g; ASTM D-1525