SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Carbon Fiber Reinforced
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.

Physical Properties	Metric	English	Comments
Density	1.55 g/cc	0.0560 lb/inÂ³	ISO 1183
	1.56 g/cc	0.0564 lb/inÂ³	ASTM D792
Moisture Absorption	0.300 %	0.300 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0070 cm/cm @Time 86400 sec	0.0070 in/in @Time 24.0 hour	ASTM D955
	0.0073 cm/cm @Time 86400 sec	0.0073 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	87.0 MPa	12600 psi	ASTM D638
	88.0 MPa	12800 psi	ISO 527
Tensile Strength, Yield	87.0 MPa	12600 psi	ASTM D638
	88.0 MPa	12800 psi	ISO 527
Elongation at Break	0.70 %	0.70 %	ASTM D638
	0.70 %	0.70 %	ISO 527
Elongation at Yield	0.70 %	0.70 %	ASTM D638
	0.70 %	0.70 %	ISO 527
Tensile Modulus	15.51 GPa	2250 ksi	1 mm/min; ISO 527
	17.23 GPa	2499 ksi	50 mm/min; ASTM D638
Flexural Strength	110 MPa	16000 psi	ASTM D790
	117 MPa	17000 psi	ISO 178
Flexural Modulus	13.1 GPa	1900 ksi	ASTM D790
	15.0 GPa	2180 ksi	ISO 178
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in	ASTM D256
Izod Impact, Unnotched	2.67 J/cm	5.00 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	3.00 kJ/mÂ²	1.43 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	16.0 kJ/mÂ²	7.61 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	4.00 J	2.95 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	1.00 J	0.738 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.35	0.35	ASTM D3702 Modified
Coefficient of Friction, Static	0.32	0.32	ASTM D3702 Modified
K (wear) Factor	139 x 10^-8 mmÂ³/N-M	69.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	66.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	36.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	66.6 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	37.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	27.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	15.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	27.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	15.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	175 Â°C	347 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	175 Â°C @Thickness 3.20 mm	347 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	170 Â°C	338 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	171 Â°C @Thickness 3.20 mm	340 Â°F @Thickness 0.126 in	unannealed; ASTM D648