SABIC Innovative Plastics LNP FARADEX NX07330 PC+ABS (Asia Pacific)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP FARADEX
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP FARADEX NX07330 PC+ABS (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Faradex NX07330 is a compound based on PC+ABS blend resin containing stainless steel and glass fiber. Added features of this material include EMI/RFI Shielding and ESD.

Physical Properties	Metric	English	Comments
Density	1.33 g/cc	0.0480 lb/in³	ASTM D792
	1.33 g/cc	0.0480 lb/in³	ISO 1183
Moisture Absorption	0.200 %	0.200 %	23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0059 cm/cm	0.0059 in/in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0064 cm/cm	0.0064 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	47.0 MPa	6820 psi	Type I, 5 mm/min; ASTM D638
	47.0 MPa	6820 psi	ISO 527
Elongation at Break	2.9 %	2.9 %	Type I, 5 mm/min; ASTM D638
	3.1 %	3.1 %	5 mm/min; ISO 527
	6.4 %	6.4 %	Flexural Strain, break, 2 mm/min; ISO 178
Tensile Modulus	3.80 GPa	551 ksi	1 mm/min; ISO 527
	3.90 GPa	566 ksi	5 mm/min; ASTM D638
Flexural Strength	77.0 MPa	11200 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength	79.0 MPa	11500 psi	1.3 mm/min, 50 mm span; ASTM D790
	87.0 MPa	12600 psi	2 mm/min; ISO 178
Flexural Modulus	3.60 GPa	522 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	1.17 J/cm	2.19 ft-lb/in	ASTM D256
	0.660 J/cm @Temperature -30.0 °C	1.24 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Unnotched	7.90 J/cm	14.8 ft-lb/in	ASTM D4812
	6.04 J/cm @Temperature -30.0 °C	11.3 ft-lb/in @Temperature -22.0 °F	ASTM D4812
Izod Impact, Notched (ISO)	11.0 kJ/m²	5.23 ft-lb/in²	80104; ISO 180/1A
	7.00 kJ/m² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	70.0 kJ/m²	33.3 ft-lb/in²	80104; ISO 180/1U
	52.0 kJ/m² @Temperature -30.0 °C	24.7 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1U
Charpy Impact, Notched	1.10 J/cm²	5.23 ft-lb/in²	ISO 179/2C
Dart Drop, Total Energy	19.0 J @Temperature 23.0 °C	14.0 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	31.0 µm/m-°C @Temperature 23.0 - 60.0 °C	17.2 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
	32.0 µm/m-°C @Temperature -40.0 - 40.0 °C	17.8 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
CTE, linear, Transverse to Flow	71.0 µm/m-°C @Temperature -40.0 - 40.0 °C	39.4 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	74.0 µm/m-°C @Temperature 23.0 - 60.0 °C	41.1 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	124 °C	255 °F	Flatw 80104 sp=64mm; ISO 75/Af
	122 °C @Thickness 3.20 mm	252 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	143 °C	289 °F	Rate B/50; ASTM D1525
	143 °C	289 °F	Rate B/50; ISO 306
	144 °C	291 °F	Rate B/120; ISO 306
	144 °C	291 °F	Rate A/50; ASTM D1525

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+6 - 1.00e+9 ohm-cm	1.00e+6 - 1.00e+9 ohm-cm	ASTM D257
Surface Resistance	10000 - 1.00e+6 ohm	10000 - 1.00e+6 ohm	ASTM D257
Shielding Effectiveness	30 - 38 dB @Thickness 3.00 mm	30 - 38 dB @Thickness 0.118 in	SABIC Method