Arkema Group Oroglas® HFI-10 Acrylic, Impact Grade  (discontinued **)

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Oroglas® HFI-10 Acrylic, Impact Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
OROGLAS HFI-10 is an impact grade that in addition to its superior impact resistance provides an improvement in flow which contribute to improve molding behavior and reduce cycle time.Key features : impact resistance: up to 10 times more impact-resistant than standard acrylic easy processing: flow significantly improved which contribute to reduce cycle time by 20 %. ( MFI, 230°c/3.8 kg ) = 3 gr / 10 min ( MVI, 230°c/3.8 kg ) = 2.8 ml / 10 min excellent optical properties with low edge color UV stability Typical applications : OROGLAS HFI-10 can be injection molded or extruded in any type of machine Typical applications are in the fields of: building, lighting, appliances, information technology, and business machines. OROGLAS HFI-10 is recommended when toughness and increased flow are required.ISO data provided by the manufacturer, Arkema.Arkema, formed in 2004, was formerly Atofina Chemicals and before that Elf Atochem.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
Water Absorption 2.0 %
2.0 %
Moisture Absorption at Equilibrium 0.36 %
0.36 %
Humidity Absorption
Melt Flow 2.8 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.8 g/10 min

@Load 8.38 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 42.0 MPa
6090 psi
50 mm/min
Elongation at Break 30 %
30 %
Nominal Strain; 50 mm/min
Elongation at Yield 5.0 %
5.0 %
50 mm/min
Tensile Modulus 1.70 GPa
247 ksi
1 mm/min
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Tensile Creep Modulus, 1 hour 1400 MPa
203000 psi
Tensile Creep Modulus, 1000 hours 1000 MPa
145000 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C

@Temperature 20.0 °C
55.6 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
Vicat Softening Point 84.0 °C
183 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Optical Properties Metric English Comments
Transmission, Visible 80 %
80 %
Mfr. reports 'Transparent' but doesn't quantify.
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 3.2

@Frequency 1e+6 Hz
3.2

@Frequency 1e+6 Hz
3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
Dielectric Strength 15.0 kV/mm
381 kV/in
Dissipation Factor 0.040

@Frequency 1e+6 Hz
0.040

@Frequency 1e+6 Hz
0.050

@Frequency 100 Hz
0.050

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V