SABIC Innovative Plastics LNP COLORCOMP WX96084 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP WX96084 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* COLORCOMP* WX96084 is a compound based on Polybutylene Terephalate resin. Added features include: Custom Color White.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.023 cm/cm | 0.023 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 26.3 % | 26.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 63.0 MPa | 9140 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 140 kJ/m² | 66.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 113 µm/m-°C @Temperature 23.0 - 60.0 °C |
62.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 23.0 - 60.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
Users viewing this material also viewed the following:
- KB Alloys 2.5% Beryllium Aluminum Alloy
- Huntsman KRYSTALFLEX® PE 505 Polyurethane Optical Aliphatic Film
- Karina 924D10/349-IS White PVC Compound
- SABIC Innovative Plastics Xenoy® X4850 PBT+PC
- SABIC Innovative Plastics LNP Thermocomp MX96070 PP (Europe-Africa-Middle East)
- Tipco Tipcofil® AG 600 - 30% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
- Ensinger Tecapeek® XP-181 Compression Molded PPEK Compound, EWS Filled and Carbon Fiber Reinforced
- Aptek 2201-A/B Fast set urethane adhesive
- Axiall 14880 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved