LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 11
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
Method A; ASTM D792
Water Absorption 0.10 %
0.10 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0070 cm/cm
0.0060 - 0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 134 MPa
19400 psi
ASTM D638
Tensile Strength, Yield 134 MPa
19400 psi
ASTM D638
Elongation at Break 6.2 %
6.2 %
ASTM D638
Elongation at Yield 5.3 %
5.3 %
ASTM D638
Tensile Modulus 7.38 GPa
1070 ksi
ASTM D638
Flexural Strength 193 MPa
28000 psi
ASTM D790
Flexural Modulus 6.21 GPa
901 ksi
ASTM D790
Izod Impact, Notched 2.56 J/cm

@Thickness 3.18 mm
4.80 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 14.3 J/cm

@Thickness 3.18 mm
26.8 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 25.3 kJ/m²
12.0 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 87.8 kJ/m²
41.8 ft-lb/in²
ISO 180
Falling Dart Impact 16.7 J
12.3 ft-lb
ASTM D3763
Impact Test 6.72 J
4.96 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 34.0 µm/m-°C

@Temperature 20.0 °C
18.9 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 99.0 µm/m-°C

@Temperature 20.0 °C
55.0 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi) 178 °C
352 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 227 - 260 °C
441 - 500 °F
Mold Temperature 43.3 - 51.7 °C
110 - 125 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi