SABIC Innovative Plastics LNP Thermocomp TX88477 PU

Category Polymer , Thermoplastic , Polyurethane, TP
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp TX88477 PU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* TX88447 is a compound based on Polyurethane resin containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ASTM D 792
1.50 g/cc
0.0542 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.23 %
0.23 %
23°C / 50% RH; ISO 62
0.17 %

@Time 86400 sec
 0.17 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.020 - 0.040 cm/cm

@Time 86400 sec
 0.020 - 0.040 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.020 - 0.040 cm/cm

@Time 86400 sec
 0.020 - 0.040 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 71.0 MPa
10300 psi
5 mm/min; ISO 527
72.0 MPa
10400 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 73.0 MPa
10600 psi
5 mm/min; ISO 527
76.0 MPa
11000 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 9.6 %
9.6 %
Type I, 5 mm/min; ASTM D 638
10 %
10 %
5 mm/min; ISO 527
Elongation at Yield 6.7 %
6.7 %
Type I, 5 mm/min; ASTM D 638
6.9 %
6.9 %
5 mm/min; ISO 527
Tensile Modulus 4.32 GPa
627 ksi
1 mm/min; ISO 527
5.79 GPa
840 ksi
50 mm/min; ASTM D 638
Flexural Strength 77.0 MPa
11200 psi
ISO 178
Flexural Modulus 3.31 GPa
480 ksi
2 mm/min; ISO 178
3.34 GPa
484 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.60 J/cm

@Temperature 23.0 °C
 3.00 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 11.9 J/cm

@Temperature 23.0 °C
 22.3 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 73.0 kJ/m²

@Temperature 23.0 °C
 34.7 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
16.0 J

@Temperature 23.0 °C
 11.8 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 33.5 µm/m-°C

@Temperature -30.0 - 30.0 °C
 18.6 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 138 µm/m-°C

@Temperature -30.0 - 30.0 °C
 76.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 187 °C
369 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
189 °C

@Thickness 3.20 mm
 372 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
101 °C

@Thickness 3.20 mm
 214 °F

@Thickness 0.126 in
 unannealed; ASTM D 648