- Shinkong Synthetic Fibers Shinite® D202G30 PBT, 30% Glass Filled, Fire Retardant
Shinkong Synthetic Fibers Shinite® D202G30 PBT, 30% Glass Filled, Fire Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Shinkong Synthetic Fibers Corp |
| Trade Name | Shinite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® D202G30 PBT, 30% Glass Filled, Fire Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 127 MPa | 18500 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 191 MPa | 27700 psi | ASTM D790 |
| Flexural Modulus | 9.32 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.65 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 | 4.0 | ASTM D150 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Nabaltec APYRAL® AOH 20 AlO(OH) Boehmite
- LG Chemical LUPOL HI2202B PP+GF20%, High Impact
- Mitsubishi Xantar® C CM 506 U Polycarbonate/ABS Blend
- SABIC Innovative Plastics NORYL SE1X PPE+PS (Asia Pacific)
- Zylog Neoplast® 240 FT EB Thermoplastic Vulcanizate
- Hippe SI MP 21 Mica Paper Reinforced Silicone Resin - Round, Rolled Tube
- Dymax 912 Strain Relief, Wire and Parts Tacking Adhesive
- 3M 21825 Industrial Polyethylene Temporary Surface Protection Tape
- Beijing Ranger Chem E-39D Semi Solid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved