SABIC Innovative Plastics GELOY XP7550 ASA+PC

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY XP7550 ASA+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection molding ASA-PC Blend suitable for exterior applications featuring outdoor weatherability, toughness, good heat performance and excellent flow.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Moisture Absorption 0.300 %
0.300 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.80 %
0.80 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 14 g/10 min

@Load 10.0 kg,
Temperature 220 °C
14 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Melt Index of Compound 26 g/10 min

@Load 5.00 kg,
Temperature 260 °C
26 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109
109
ASTM D785
Tensile Strength at Break 44.0 MPa
6380 psi
Type I, 50 mm/min; ASTM D638
44.0 MPa
6380 psi
50 mm/min; ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 37 %
37 %
50 mm/min; ISO 527
40 %
40 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.8 %
3.8 %
50 mm/min; ISO 527
4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.55 GPa
370 ksi
5 mm/min; ASTM D638
2.55 GPa
370 ksi
1 mm/min; ISO 527
Flexural Yield Strength 74.0 MPa
10700 psi
2 mm/min; ISO 178
82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
2.48 GPa
360 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.75 J/cm
7.03 ft-lb/in
ASTM D256
0.530 J/cm

@Temperature -30.0 °C
0.993 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 4.00 J/cm²
19.0 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 10.0 J

@Temperature -30.0 °C
7.38 ft-lb

@Temperature -22.0 °F
ASTM D3763
36.0 J

@Temperature 23.0 °C
26.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Hot Ball Pressure Test 85.0 °C
185 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 103 °C
217 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
104 °C

@Thickness 3.20 mm
219 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
192 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
89.0 °C

@Thickness 3.20 mm
192 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 105 °C
221 °F
Rate B/50; ASTM D1525
105 °C
221 °F
Rate B/50; ISO 306
106 °C
223 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Gloss 94 %
94 %
untextured, 60 degrees; ASTM D523